An interesting practical experiment about the preparation of dye–sensitized solar cells (DSSC) using natural dyes were carried out by the undergraduate students in the chemistry course at UNICAMP . Natural dyes were extracted from blueberries (Vaccinium myrtillus L.), jabuticabas (Myrciaria cauliflora), raw and cooked beets (Beta vulgaris L.), and annattos (Bixa orellana L.), which were used to sensitize TiO2 films that composed the photoanode in the DSSC. A polymer electrolyte containing an iodide/triiodide redox couple was used in lieu of the use of liquid solutions to prevent any leakage in the devices. A maximum solar-to-electric energy conversion of 0.26 ± 0.02% was obtained for the solar cell prepared with annatto extracts. This experiment was an effective way to illustrate to the undergraduate students how to apply some of the chemical concepts that they learned during their chemistry course to produce electric energy from a clean and renewable energy source. Teachers could also exploit the basics of the electronic transitions in inorganic and organic compounds (e.g., metal-to-ligand charge transfer and ϖ-ϖ* transitions), thermodynamics (e.g., Gibbs free energy), acid–base reactions in the oxide solid surface and electrolyte, and band theory (i.e., the importance of the Fermi level energy).

Glioxal pode ser obtido a partir de biomassa (como da oxidação de lipídeos) e não é tóxico ou volátil, tendo sido por isso utilizado no presente trabalho como substituto de formaldeído na preparação de resina fenólica do tipo novolaca, sendo usado como catalisador o ácido oxálico, que também pode ser obtido de fontes renováveis. A resina glioxal-fenol foi utilizada na preparação de compósitos reforçados com celulose microcristalina (CM, 30, 50 e 70% em massa), uma celulose com elevada área superficial. As imagens de microscopia eletrônica de varredura (MEV) das superfícies fraturadas demonstraram que os compósitos apresentaram boa interface reforço/matriz, consequência da elevada área superficial da CM e presença de grupos polares (hidroxilas) tanto na matriz como na celulose, o que permitiu a formação de ligações hidrogênio, favorecendo a compatibilidade entre ambas. A análise térmica dinâmico-mecânica (DMTA) demonstrou que todos os compósitos apresentaram elevado módulo de armazenamento à temperatura ambiente. Além disso, o compósito reforçado com 30% de CM apresentou baixa absorção de água, comparável à do termorrígido fenólico, que é utilizado em escala industrial. Os resultados demonstraram que compósitos com boas propriedades podem ser preparados usando elevada proporção de materiais obtidos de biomassa.

Glyoxal, which can be obtained from biomass (as by lipids oxidation), is non-toxic and non-volatile. It was used as a substitute of formaldehyde, which does not have these properties, in the synthesis of a novolac-type phenolic resin, using oxalic acid as a catalyst, which can also be obtained from renewable sources. The glyoxal-phenol resin was used in the preparation of composites reinforced with microcrystalline cellulose (MCC 30, 50, and 70% w/w). Scanning electron microscopy (SEM) images of the fractured surfaces showed that the composites presented a good reinforcement/matrix interface. This can be attributed to the high surface area of the MCC and also to the presence of polar groups (hydroxyl) in both cellulose and matrix, which allowed the formation of hydrogen bonds, leading to a good adhesion between the components present at the interface. Dynamic mechanical thermoanalysis (DMTA) showed that all of the obtained composites have high storage modulus at room temperature. Moreover, the composite reinforced with 30% of MCC showed the lowest water absorption, almost the same as that of the phenolic thermoset, which is used in industrial applications. The results showed that composites with good properties can be prepared using high proportions of materials obtained from biomass.